Adhesion performance and film formation of acrylic emulsion coating on medium density fiberboard treated with Ar plasma

Auteur(s): Gonzalez de Cademartori, Pedro Henrique; Roani de Carvalho, Agne; Dantas Marangoni, Paulo Roberto; Coelho Berton, Marcos Antonio; Blanchet, Pierre; Bolzon de Muniz, Graciela Ines; Esteves Magalhães, Washington Luiz
Résumé: This work investigates the adhesion properties of medium density fiberboard (MDF) panel surfaces treated by an argon plasma at two power levels (50 and 150 W) and four glow discharge times (10, 40, 60 and 120 s) and then coated with an acrylic emulsion. Wettability parameters and film formation kinetics were investigated by water apparent contact angle and diffusing wave spectroscopy, respectively. Pull-off strength was used to determine coating/wood adhesion. The aging effect of 300-days in storage at ambient conditions was examined by apparent contact angle measurements. The wettability of the MDF surface was enhanced significantly - especially at the 150 W power level – that improves coating/wood adhesion. A film formation process occurred in shorter time for plasma treated samples due to the faster motion of particles. MDF panels partially recovered their natural hydrophobicity in the first ten days of storage. Nevertheless, higher levels of power and time of glow discharge were able to slow down the aging effects.
Type de document: Article de recherche
Date de publication: 28 juillet 2016
Date de la mise en libre accès: Accès restreint
Version du document: VoR
Lien permanent: http://hdl.handle.net/20.500.11794/13701
Ce document a été publié dans: International Journal of Adhesion and Adhesives, Vol. 70, 322–328 (2016)
https://doi.org/10.1016/j.ijadhadh.2016.08.002
Butterworth-Heinemann Ltd.
Autre version disponible: 10.1016/j.ijadhadh.2016.08.002
Collection :Articles publiés dans des revues avec comité de lecture

Fichier(s) :
Description TailleFormat 
1-s2.0-S0143749616301543-main - Final version.pdf
1.15 MBAdobe PDF    Demander une copie
Tous les documents dans CorpusUL sont protégés par la Loi sur le droit d'auteur du Canada.